PROPIEDADES | ESPECIFICACIONES | NORMA | |
Mín. | Máx. | ||
Densidad aparente, g/cm3 | 2.97 | 3.12 | ISO 3923-1 |
Tiempo de derrame, s/50g | – | 30 | ISO 4490 |
GRANULOMETRÍA DEL POLVO DE BASE, (PESO %) | ESPECIFICACIONES | NORMA | ||||
U.S. MESH | MICRONS | Mín. | Máx. | |||
+60 | +250 | – | 0.1 | ISO 4497 | ||
-60 | +100 | -250 | +150 | – | 18.0 | ISO 4497 |
-325 | -45 | 10.0 | 30.0 | ISO 4497 |
COMPOSICIÓN QUÍMICA DEL POLVO DE BASE, (PESO %) | ESPECIFICACIONES | NORMA | |
Mín. | Máx. | ||
Carbono | – | 0.010 | ASTM E 1019 |
Oxígeno | – | 0.15 | ASTM E 1019 |
Azufre | – | 0.014 | ASTM E 1019 |
Manganeso | 0.10 | 0.18 | ASTM E 322 |
Molibdeno | 1.35 | 1.65 | ASTM E 322 |
Niquel | 3.60 | 4.40 | ASTM E 322 |
Cobre | 1.80 | 2.20 | ASTM E 322 |
PROPIEDADES DE COMPACTACIÓN, (1) | ESPECIFICACIONES | NORMA | |
Mín. | Máx. | ||
Densidad a 600 MPa, (g/cm³) | 7.00 | – | ISO 3927 |
Resistencia en verde a 600 MPa, (MPa) | 10.0 | – | ISO 3995 |